Package Size: 0
Reference Number:
- 1
Prepare
Ensure resin is at room temperature, protected from light, and it is stirred before use.
- 2
Print
Use DLP, LCD, or SLA technology to print the material in layers up to 150 microns as per printer capabilities.
Suggested Devices:
- SLA printers
- DLP
- LCD
- 3
Wash
Wash the printed parts in IPA for 5 minutes to remove any uncured resin.
- 4
Post-Cure
Use Otoflash® G171-6 under Nitrogen atmosphere with 2x 2000 flashes of xenon lamp per second, 200 W for post-curing process.
Suggested Devices:
- Otoflash® G171-6
| Property | Value | Unit | Test Condition |
|---|---|---|---|
| Flexural strength/ modulus of rupture | 83 | MPa | |
| Flexural Modulus/ Bending module | 2200 | MPa | |
| Deflection at Fracture | 10 | % | |
| Tensile Strength | 51 | MPa | |
| Tensile Modulus | 2500 | MPa | |
| Elongation at Break | 7 | % | |
| Shore hardness | 85 | D | |
| Viscosity | 710 | mPa∙s | @ 25 °C |
| Density | 1.1 | g/mL | |
| Critical Energy 405 nm (Ec) | 3.9 | mJ/cm2 | |
| Critical Energy 385 nm (Ec) | 4.7 | mJ/cm2 | |
| Depth of Penetration 405 nm | 0.19 | mm | |
| Depth of Penetration 385 nm | 0.12 | mm | |
| HDT B | 70 | °C | |
| Printing Technology | DLP LCD SLA |