Package Size: 0
Reference Number:
- 0
prepare
Prepare the 3D printer with necessary settings and ensure you have sufficient resin and washing agents available.
- 1
print
Print the design using DLP, LCD or SLA technology with the specified settings.
Suggested Devices:
- SLA Printers
- DLP Printers
- LCD Printers
- 2
wash
Wash the printed part using IPA or Ethanol to remove residual resin.
- 3
post-cure
Post-cure the washed parts using UV light to ensure maximum strength and stability.
| Property | Value | Unit | Test Condition |
|---|---|---|---|
| Flexural strength/ modulus of rupture | 82 | MPa | |
| Flexural Modulus/ Bending module | 2300 | MPa | |
| Deflection at Fracture | 3.5 | % | |
| Tensile Strength | 57 | MPa | |
| Tensile Modulus | 2600 | MPa | |
| Elongation at Break | 4.3 | % | |
| Shore hardness | 82 | D | |
| Viscosity | 185 | mPa·s | @ 25 °C |
| Density | 1.05 | g/mL | |
| Critical Energy 405 nm (Ec) | 4.5 | mJ/cm2 | |
| Critical Energy 385 nm (Ec) | 5.7 | mJ/cm2 | |
| Depth of Penetration 405 nm | 0.14 | mm | |
| Depth of Penetration 385 nm | 0.11 | mm | |
| HDT B | 59 | °C | |
| Izod notched | 15 | J/m | |
| Storage Max Temp | 28 | °C | |
| Minimum Wall Thickness | 200 | μm | |
| Detergent | Isopropyl alcohol PC | ||
| Printing Technology | SLA DLP LCD |