Package Size: 0
Reference Number:
- 1
Prepare
Prepare the printing setup with required resin and equipment.
- 2
Print
Use DLP, LCD, or SLA printers for printing.
Suggested Devices:
- SLA Printer
- DLP Printer
- LCD Printer
- 3
Wash
Wash using IPA or Ethanol as a detergent to remove any uncured resin.
- 4
Post-Cure
UV post-cure the printed parts for final properties.
Suggested Devices:
- UV Curing Chamber
| Property | Value | Unit | Test Condition |
|---|---|---|---|
| Flexural strength/ modulus of rupture | 93 | MPa | |
| Flexural Modulus/ Bending module | 2500 | MPa | |
| Deflection at Fracture | 3.5 | % | |
| Tensile Strength | 55 | MPa | |
| Tensile Modulus | 2700 | MPa | |
| Elongation at Break | 4.4 | % | |
| Shore hardness | 85 | D | |
| Viscosity | 160 | mPa∙s | @ 25 °C |
| Density | 1.05 | g/mL | |
| Critical Energy 405 nm (Ec) | 5 | mJ/cm2 | |
| Critical Energy 385 nm (Ec) | 4.6 | mJ/cm2 | |
| Depth of Penetration 405 nm | 0.35 | mm | |
| Depth of Penetration 385 nm | 0.21 | mm | |
| HDT B | 123 | °C | |
| Dielectric Strength | 25 | kV/mm | |
| Volume Resistivity | 18000000 | Ωcm | |
| Izod notched | 22 | J/m | |
| Tear Strength | 120 | kN/m | |
| Water absorption | 0.3 | % | 24h, 23 °C |
| Storage Min Temp | 21 | °C | |
| Storage Max Temp | 28 | °C | |
| Minimum Wall Thickness | 200 | μm | Mold |
| Flammability UL 94 | V-0 | ||
| Detergent | Isopropyl alcohol | ||
| Printing Technology | DLP LCD SLA OTHER |