Package Size: 0
Reference Number:
- 1
Prepare
Ensure room temperature storage and protection from light. Stir material before using.
- 2
Print
Use on DLP, LCD, or SLA printers with a standard grey color. More colors available upon request.
Suggested Devices:
- LCD Printers
- SLA Printers
- DLP Printers
- 3
Wash
Wash printed parts using Isopropyl alcohol (IPA).
- 4
Post-Cure
Post-cure the printed part with UV light or LEDs for one hour at 405 nm.
| Property | Value | Unit | Test Condition |
|---|---|---|---|
| Flexural strength/ modulus of rupture | 42 | MPa | |
| Flexural Modulus/ Bending module | 1200 | MPa | |
| Deflection at Fracture | 6 | % | |
| Tensile Strength | 32 | MPa | 250 mm/min; 35 mm/min |
| Tensile Modulus | 1200 | MPa | 250 mm/min; 35 mm/min |
| Elongation at Break | 19 | % | 250 mm/min; 35 mm/min |
| Shore hardness | 76 | D | |
| Viscosity | 103 | mPa∙s | @25 °C |
| Density | 1.07 | g/mL | |
| Critical Energy 405 nm (Ec) | 2.4 | mJ/cm2 | |
| Critical Energy 385 nm (Ec) | 2.8 | mJ/cm2 | |
| Depth of Penetration 405 nm | 0.12 | mm | |
| Depth of Penetration 385 nm | 0.08 | mm | |
| Izod notched | 24 | J/m | |
| Detergent | Isopropyl alcohol | ||
| Printing Technology | DLP LCD SLA |