Package Size: 0
Reference Number:
- 1
Prepare
Ensure printer is set up with the correct settings for the material and the environment is suitable for printing.
- 2
Print
Use DLP, LCD, or SLA printing technology to fabricate the model. Ensure layers are thin for high precision.
Suggested Devices:
- DLP 3D Printers
- SLA 3D Printers
- LCD 3D Printers
- 3
Wash
Clean the printed part using IPA detergent to remove any uncured resin.
- 4
Post-cure
Expose the printed part to UV light at low intensity for 60 minutes at 405 nm for full curing.
| Property | Value | Unit | Test Condition |
|---|---|---|---|
| Tensile Strength | 37 | MPa | 25 mm/min |
| Tensile Modulus | 1900 | MPa | 25 mm/min |
| Elongation at Break | 8 | % | 25 mm/min |
| Shore hardness | 80 | ||
| Viscosity | 171 | mPa∙s | @ 25 °C |
| Density | 1.05 | g/mL | |
| Critical Energy 405 nm (Ec) | 4.3 | mJ/cm2 | |
| Critical Energy 385 nm (Ec) | 5.3 | mJ/cm2 | |
| Depth of Penetration 405 nm | 0.08 | mm | |
| Depth of Penetration 385 nm | 0.1 | mm | |
| HDT B | 52 | °C | |
| Izod notched | 17 | J/m | |
| Water absorption | 0.3 | % | |
| Storage Max Temp | 28 | °C | |
| Detergent | Isopropyl alcohol | ||
| Printing Technology | DLP LCD SLA |