Package Size: 1 kg
Reference Number: R59B
- 1
Preparation
Ensure the working environment is clean and free from contaminants.
- 2
Printing
Load the resin into the printer and set parameters as per material specifications.
Suggested Devices:
- Mars Pro
- Mars
- Photon Mono
- Photon
- 3
Washing
Wash the printed part in isopropyl alcohol for 5 minutes.
- 4
Drying
Allow the part to dry naturally or use a gentle air stream.
- 5
Post-curing
Cure the printed part for 20 minutes at 60°C under UV light.
Suggested Devices:
- Mercury Plus
- Wash & Cure Station
| Property | Value | Unit | Test Condition |
|---|---|---|---|
| Flexural strength/ modulus of rupture | 80 | MPa | Standard Laboratory Conditions |
| Flexural Modulus/ Bending module | 2100 | MPa | Standard Laboratory Conditions |
| Deflection at Fracture | 3.5 | % | Standard Laboratory Conditions |
| Tensile Strength | 50 | MPa | Standard Laboratory Conditions |
| Tensile Modulus | 1800 | MPa | Standard Laboratory Conditions |
| Elongation at Break | 7 | % | Standard Laboratory Conditions |
| Yield Strength | 45 | MPa | Standard Laboratory Conditions |
| Shore hardness of green body | 85 | A | Standard Laboratory Conditions |
| Shore hardness | 88 | D | Standard Laboratory Conditions |
| Viscosity | 500 | cP | @ 25 °C |
| Density | 1.1 | g/cm³ | Standard Laboratory Conditions |
| Critical Energy 405 nm (Ec) | 8 | mJ/cm² | 405 nm |
| Depth of Penetration 405 nm | 0.1 | mm | 405 nm |
| HDT A | 60 | °C | 1.8 MPa |
| HDT B | 70 | °C | 0.45 MPa |
| Tg | 80 | °C | Standard Laboratory Conditions |
| CTE (-50°C,60°C) | 80 | µm/mK | (-50°C,60°C) |
| CTE (90°C,200°C) | 120 | µm/mK | (90°C,200°C) |
| Heat Specific Capacity | 1.45 | J/gK | @ 20 °C |
| Dielectric Strength | 20 | kV/mm | Short Voltage |
| Relative Permittivity | 3.8 | - | @ 1 kHz |
| Dissipation Factor | 0.02 | - | @ 1 kHz |
| Volume Resistivity | 10000000000000000 | ohm·cm | Standard Laboratory Conditions |
| Volume Resistivity after 7d | 100000000000000 | ohm·cm | After 7 days @ RT H2O |
| Izod notched | 5 | kJ/m² | @ 23 °C |
| Tear Strength | 40 | kN/m | Standard Laboratory Conditions |
| Water absorption | 0.5 | % | 24 hours @ 23 °C |
| Storage Min Temp | 5 | °C | |
| Storage Max Temp | 35 | °C | |
| Minimum Wall Thickness | 0.5 | mm | |
| Temperature | 60 | °C | |
| Layer Thickness Min | 0.01 | mm | |
| Layer Thickness Max | 0.1 | mm | |
| Print Temperature | °C | ||
| Flammability UL 94 | V-2 | ||
| Detergent | Isopropyl alcohol | ||
| Printing Technology | SLA DLP | ||
| UV wavelength | 405.0nm |